Título:	Evaluación de mezclas de polihidroxibutirato (P3HB) con aditivos para la obtención de un material polimérico
Otros títulos:	Evaluation of mixtures of polyhydroxybutyrate (P3HB) with additives to obtain a polymeric material
Autor(es):	Rámirez Peréz, Laura Ángelica Sánchez Vargas, Daniela
Director de tesis:	Ramos Farfán, Andrés Felipe
Tipo de licencia:	Atribución – No comercial
Palabras clave:	Aditivos;Polihidroxibutirato (P3HB);Fundición con solvente;Biopolímeros;Additives;Solvent casting;Biopolymers;Polyhydroxybutyrate;Tesis y disertaciones académicas
Fecha de publicación:	5-nov-2019
Editorial:	Fundación Universidad de América
Resumen:	Este proyecto pretende evaluar aquellos aditivos que presentan compatibilidad y favorezcan las propiedades fisicoquímicas del P3HB,de manera que se seleccionaron los aditivos ácido poliláctico (PLA), polietilenglicol 400 (PEG 400) y celulosa nanocristalina (CNC), con los que se realizaron mezclas binarias y ternarias a diferentes concentraciones y temperaturas; las mezclas fueron realizadas a partir de la técnica de solvent casting donde se usó el cloroformo para diluir tanto el P3HB como los aditivos. Una vez realizadas las blendas se caracterizaron mediante las pruebas de análisis termogravimétrico (TGA) y calorimetría diferencial de barrido (DSC); aquellas que mostraron resultados favorables se les determinó la resistencia a partir de una prueba mecánica de tensión. En cuanto al material compuesto que se obtuvo, se demostró que el CNC no mostró gran afinidad, mientras que el PLA presentó alta compatibilidad con el P3HB. De igual manera el plastificante (PEG) ocasionó una mejora en las propiedades térmicas, aunque a pesar de esto, al analizar el efecto en las propiedades mecánicas para las blendas de P3HB/PLA/PEG se tuvo un efecto desfavorable a comparación con aquellas mezclas de P3HB/PLA sin PEG. Se concluyó mediante la caracterización del material que aquel que mostró un alto punto de fusión y menor deformación fue la mezcla de P3HB/PLA a concentraciones 70/30 respectivamente. De acuerdo con estos resultados, se planteó la producción del material y se realizó un estudio de costos de materia prima, equipos, consumo energético e hídrico.
Abstract:	This project aims to evaluate those additives that have compatibility and favor the physicochemical properties of P3HB, so that the additives were selected polylactic acid (PLA), polyethylene glycol 400 (PEG 400) and nanocrystalline cellulose (CNC), with those that were binary and ternary mixtures at different concentrations and temperatures; The mixtures were made from the solvent casting technique where chloroform was used to dilute both the P3HB and the additives. Once the blenders were made, they were characterized by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) tests; those that showed favorable results resistance were determined from a mechanical stress test. As for the composite material that was obtained, it was shown that the CNC did not show great affinity, while the PLA showed high compatibility with the P3HB. Similarly, the plasticizer (PEG) caused an improvement in the thermal properties, although despite this, when analyzing the effect on the mechanical properties for the P3HB / PLA / PEG fills there was an unfavorable effect compared to those mixtures of P3HB / PLA without PEG. It was concluded by characterizing the material that the one that showed a high melting point and less deformation was the mixture of P3HB / PLA at concentrations 70/30 respectively. According to these results, the production of the material was considered and a study of costs of raw material, equipment, energy and water consumption was carried out.
URI:	http://hdl.handle.net/20.500.11839/7718
Citación:	APA 6th - Rámirez Peréz, L. Á. y Sánchez Vargas, D. (2019) Evaluación de mezclas de polihidroxibutirato (P3HB) con aditivos para la obtención de un material polimérico(Trabajo de grado). Fundación Universidad de América. Retrieved from http://hdl.handle.net/20.500.11839/7718
Aparece en las colecciones:	Trabajos de grado - Ingeniería Química

Este ítem está sujeto a una licencia Creative Commons