Título:	Evaluación de las propiedades fisicoquímicas del caucho seco y tiempo de coagulación del látex al implementar vinazas como coagulante
Otros títulos:	Evaluation of the physicochemical properties of dry rubber and latex coagulation time by using vinasse as a coagulant
Autor(es):	Peralta Cruz, Natalia Andrea
Director de tesis:	León Lozano, José David
Tipo de licencia:	Atribución – No comercial – Sin Derivar
Palabras clave:	Ácido fórmico;Caucho seco;Plasticidad;Formic acid;Dry rubber;Plasticity;Tesis y disertaciones académicas
Fecha de publicación:	7-feb-2022
Editorial:	Fundación Universidad de América
Resumen:	El presente trabajo investigativo evaluó las propiedades fisicoquímicas del caucho seco y el tiempo de coagulación del látex natural de la empresa Mavalle S.A.S. al ser coagulado con vinazas, estas son producto de la destilación de etanol a partir de la caña de azúcar. El proceso inició en el laboratorio, en donde se realizaron diferentes ensayos para establecer 3 concentraciones de vinazas para coagular el látex, sebevaluaron las propiedades fisicoquímicas del caucho seco tras 2 días de maduración en campo a dos temperaturas de secado, resultando una disminución de la Viscosidad Mooney y la plasticidad al secar la muestra a elevadas temperaturas, un comportamiento opuesto a la variación de las concentraciones, ya que al aumentar la concentración de vinazas, la plasticidad y PRI aumentan; para la verificación de los resultados se utilizó Excel y Minitab, en los cuales se planteó el diseño experimental. De los resultados obtenidos se pudo concluir que las vinazas pueden ser una sustancia adecuada para la coagulación del látex, debido a que no genera alteraciones en el material. Los resultados se encuentran dentro de los parámetros establecidos por la norma ISO 2000:2014 y las afectaciones a la salud son menores comparados con el ácido fórmico.
Abstract:	The present research work evaluated the physicochemical properties of dry rubber and the coagulation time of the natural latex of Mavalle S.A.S. and the coagulation time of the natural latex of the company Mavalle S.A.S. when coagulated with vinasse, coagulated with vinasse, which is a product of ethanol distillation from sugar cane. The process began in the laboratory, where different tests were carried out to establish 3 concentrations of stillage. different tests were carried out to establish 3 concentrations of stillage to coagulate the latex, and the physicochemical properties of the rubber were evaluated physicochemical properties of the dried rubber were evaluated after 2 days of maturation in the field at two drying temperatures drying temperatures, resulting in a decrease of Mooney Viscosity and plasticity when the sample was dried plasticity when drying the sample at high temperatures, a behavior opposite to the variation of the concentrations, since the concentrations, since as the concentration of stillage increases, plasticity and PRI increase. plasticity and PRI increase; Excel and Minitab were used to verify the results. Minitab were used to verify the results, in which the experimental design was presented. From the results obtained, it was possible to conclude that stillage can be a suitable substance for the coagulation of the suitable substance for latex coagulation, since it does not generate alterations in the material in the material. The results are within the parameters established by the ISO 2000:2014 standard the ISO 2000:2014 standard and the health effects are lower compared to formic acid.
URI:	https://hdl.handle.net/20.500.11839/8927
Citación:	APA 7th - Peralta Cruz, N. A. (2022) Evaluación de las propiedades fisicoquímicas del caucho seco y tiempo de coagulación del látex al implementar vinazas como coagulante. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/8927
Aparece en las colecciones:	Trabajos de grado - Ingeniería Química

Este ítem está sujeto a una licencia Creative Commons