Título:	Evaluación del proceso de recuperación de litio y cobalto presentes en baterías gastadas de ion-li de vehículos eléctricos e híbridos por medio de un proceso de lixiviación ácida
Otros títulos:	Evaluation of the lithium and cobalt recovery process in spent ion-li batteries of electric and hybrid vehicles by an acid leaching process
Autor(es):	Guevara Coronado, Andrés Mauricio Vargas Pérez, Stefanny
Director de tesis:	Jaimes Bastidas, Carmen Rocío
Tipo de licencia:	Atribución – No comercial
Palabras clave:	Lixiviación ácida;Litio;Cobalto;Baterias ion-litio;Acid leaching;Lithium;Cobalt;Lithium-ion batteries;Tesis y disertaciones académicas
Fecha de publicación:	12-feb-2019
Editorial:	Fundación Universidad de América
Resumen:	Baterías de ion-litio gastadas provenientes de bicicletas eléctricas, con 56 celdas electroquímicas (26 celdas rectangulares y 30 celdas cilíndricas) , fueron sujetas a un procedimiento de pretratamiento que involucra una separación física y química de los componentes de interés, obteniendo como material de partida de aproximadamente 2100 g de material activo del cátodo en forma de LiCo0.33Ni0.33Mn0.33O2, donde mediante la aplicación de una prueba de difracción de rayos X a la muestra se confirmó la presencia de este óxido en la muestra, seguidamente la muestra fue analizada mediante espectrometría de absorción atómica con llama, determinando de esta manera, la composición metálica inicial de la muestra. Simultáneamente se llevó a cabo una revisión bibliográfica con el objetivo de seleccionar el método de lixiviación ácida mediante la metodología de sumas ponderadas, donde se optó por el uso de ácido cítrico y peróxido de hidrogeno como reactivos más acordes para llevar a cabo el proceso de lixiviación.
Abstract:	Used lithium-ion batteries from electric bicycles, with 56 electrochemical cells (26 rectangular cells and 30 cylindrical cells), were subjected to a pre-treatment procedure that involves a physical and chemical separation of the components of interest, obtaining as starting material approximately 2100 g of cathode active material in the form of LiCo0.33Ni0.33Mn0.33O2, where by applying an X-ray diffraction test to the sample the presence of this oxide was confirmed, then the sample was analyzed by flame atomic absorption spectrometry , thus determining the initial metallic composition of the sample. Simultaneously, a bibliographic review was carried out with the objective of selecting the acid leaching system using the summation method where the use of citric acid and hydrogen peroxide was chosen as the most appropriate reagents to carry out the leaching process. An experimental model was developed to carry out the acid leaching in which the reaction time, citric acid concentration, leaching temperature and solid/liquid ratio were manipulated in order to obtain the optimal conditions that achieve the highest leaching efficiency.
URI:	http://hdl.handle.net/20.500.11839/7410
Citación:	APA 6th - Guevara Coronado, A. M. y Vargas Pérez, S. (2019) Evaluación del proceso de recuperación de litio y cobalto presentes en baterías gastadas de ion-li de vehículos eléctricos e híbridos por medio de un proceso de lixiviación ácida (Trabajo de grado). Fundación Universidad de América. Retrieved from http://hdl.handle.net/20.500.11839/7410
Aparece en las colecciones:	Trabajos de grado - Ingeniería Química

Este ítem está sujeto a una licencia Creative Commons