Title: Evaluación del ciclo de vida de las películas de la mezcla Tio2 /Cuo para la inactivación fotocatalítica de la E.coli en presencia de luz visible
Other Titles: Evaluation of the life cycle of the films of the Tio2 / Cuo mix for the photocatalytic inactivation of E.coli in the presence of visible light
Authors: Poveda Vargas, Paola Giselle
Thesis advisor: Quiñones Segura, César Augusto
Páez Morales, Adriana Inés
License type: Atribución – No comercial
Keywords: Fotocatálisis;Películas;Photocatalysis;Films;Tesis y disertaciones académicas
Issue Date: 18-Aug-2018
Publisher: Fundación Universidad de América
Resumen: En el presente trabajo de grado se llevó a cabo la elaboración de la mezcla de TiO2/CuO por medio de dos métodos de impregnación, en los cuales se varió la concentración de la solución precursora CuSO4, de igual manera se determinó el método de deposición por spin coating y la cantidad necesaria de suspensión a depositar. Se mantuvo la temperatura de calcinación de 600ºC establecida en el grupo de Materiales Fotoactivos. La caracterización de las mezclas se realizó por microscopía electrónica de barrido (SEM) y difracción de rayos x (DRX). Para realizar el ciclo de vida de las películas, estas fueron sometidas a pruebas de remoción de azul de metileno, las cuales comprobaron su funcionalidad. Una vez comprobada, se inicia el proceso fotodegradativo de las películas de la mezcla TiO2/CuO en presencia de la bacteria E.coli con el fin de la inactivación del microorganismo en presencia de luz visible en un tiempo estimado de 9 horas. Una vez finiquitado el tiempo se empleó el método de recuento en placa en superficie para la cuantificación de las UFC/mL obteniendo una reducción de nueve unidades logarítmicas respecto a las UFC/mL iniciales. Se obtuvieron datos del 99,99% de eliminación de la bacteria en los tres primeros usos de la película de la mezcla TiO2/CuO, en su cuarto uso se obtuvo una caída de la eficiencia del 47,85% comprobando que el método es repetible.
Abstract: In the present work of degree was carried out the elaboration of the mixture of TiO2 / CuO by means of two methods of impregnation, in which the concentration of the precursor solution CuSO4 was varied, in the same way the method of deposition by spin coating and the necessary amount of suspension to deposit. The calcination temperature of 600ºC established in the group of Photoactive Materials was maintained. The characterization of the mixtures was carried out by scanning electron microscopy (SEM) and x-ray diffraction (XRD). To realize the life cycle of the films, they were subjected to methylene blue removal tests, which proved their functionality. Once checked, the photodegradative process of the films of the TiO2 / CuO mixture begins in the presence of the E. coli bacterium in order to inactivate the microorganism in the presence of visible light in an estimated time of 9 hours. Once the time was completed, the surface plate count method was used to quantify the CFU / mL obtaining a reduction of nine logarithmic units compared to the initial CFU / mL. Data of 99.99% elimination of the bacteria was obtained in the first three uses of the TiO2 / CuO mixture film. In its fourth use, an efficiency drop of 47.85% was obtained, verifying that the method is repeatable .
URI: http://hdl.handle.net/20.500.11839/6962
Citation: APA 6th - Poveda Vargas, P. G. (2018) Evaluación del ciclo de vida de las películas de la mezcla Tio2 /Cuo para la inactivación fotocatalítica de la E.coli en presencia de luz visible (Trabajo de grado). Fundación Universidad de América. Retrieved from http://hdl.handle.net/20.500.11839/6962
Appears in Collections:Trabajos de grado - Ingeniería Química

Files in This Item:
File Description SizeFormat 
6122922-2018-2-IQ.pdf2.51 MBAdobe PDFView/Open


This item is licensed under a Creative Commons Licence Creative Commons