Title: Evaluación del efecto de la concentración de CsI sobre la morfología de Perovskitas bicatión CsX(MA1-X)Pb(I)3 sintetizadas para el uso como capa activa en celdas solares fotovoltaicas
Authors: Buitrago Gutiérrez, Jenny Paola
Thesis advisor: Quiñones Segura, César Augusto
License type: Atribución – No comercial
Keywords: Perovskita de cationes mixtos;Reflectancia difusa;Coeficiente de absorción;Gap de energía;Mixed cation perovskite;Diffuse reflectance;Absorption coefficient;Energy gap;Tesis y disertaciones académicas
Issue Date: 5-Mar-2018
Publisher: Fundación Universidad de América
Resumen: En este trabajo, se sintetizó películas delgadas de Perovskita de catión mixto CsxMA1-xPbI3 por medio de la técnica de deposición spin coating para ser usadas como capas absorbentes en celdas solares fotovoltaicas. Se evaluó el efecto de la concentración de CsI sobre las propiedades ópticas y morfológicas de películas CsxMA1-xPbI3 y se observó una evolución morfológica regular. A través de medidas de reflectancia y transmitancia difusa, se encontraron los parámetros de síntesis que aseguran para los materiales buenas propiedades en términos de gap de energía, espesor de película y coeficiente de absorción fotónica. A partir de las medidas de AFM, se evidenció el crecimiento de granos compactos de tamaño submicrométrico de CsxMA1-xPbI3. Se sugiere que la incorporación de una cantidad de Cs del 10% en la estructura CsxMA1-xPbI3 (Perovskita con durabilidad de fase superior), puede ser muy prometedor para la realización de celdas solares tipo Perovskita eficientes.
Abstract: In this work, thin films of perovskite of mixed cation CsxMA1-xPbI3 were synthesized by means of the spin coating deposition technique to be used as absorptive layers in photovoltaic solar cells. The effect of the CsI concentration on the optical and morphological properties of CsxMA1-xPbI3 films was evaluated and a regular morphological evolution was observed. Through reflectance and diffuse transmittance measurements, the synthesis parameters were found that ensure good properties for the materials in terms of energy gap, film thickness and photonic absorption coefficient. From the measurements of AFM, the growth of compact grains of submicrometric size of CsxMA1-xPbI3 was evidenced. It is suggested that the incorporation of a quantity of Cs of 10% in the structure CsxMA1-xPbI3 (Perovskite with superior phase durability), can be very promising for the realization of efficient Perovskite type solar cells.
URI: http://hdl.handle.net/20.500.11839/6698
Citation: APA 6th - Buitrago Gutiérrez, J. P. (2018) Evaluación del efecto de la concentración de CsI sobre la morfología de Perovskitas bicatión CsX(MA1-X)Pb(I)3 sintetizadas para el uso como capa activa en celdas solares fotovoltaicas (Trabajo de grado). Fundación Universidad de América. Retrieved from http://hdl.handle.net/20.500.11839/6698
Appears in Collections:Trabajos de grado - Ingeniería Química

Files in This Item:
File Description SizeFormat 
6131960-2018-1-IQ.pdf1.6 MBAdobe PDFView/Open


This item is licensed under a Creative Commons Licence Creative Commons