Title: Validación del efecto de la concentración de óxido de cobre (x) en mezcla con dióxido de titanio (tio2)(1-x) (cuo)(x) para la inactivación fotocatalítica de e. coli en presencia de luz visible
Authors: Bohórquez Moreno, Paula Melissa
Gamboa Borrego, María Camila
Thesis advisor: Quiñones Segura, César Augusto
Páez Morales, Adriana Inés
License type: Atribución – No comercial
Keywords: Fotocatálisis heterogénea;Dióxido de titanio;Oxido de cobre;Heterogeneous photocatalysis;Titanium dioxide;Copper oxide;Tesis y disertaciones académicas
Issue Date: 28-Feb-2018
Publisher: Fundación Universidad de América
Resumen: En este proyecto se validó que películas de dióxido de titanio en mezcla con óxido de cobre inactivaran el 99,99% la bacteria E. coli siguiendo la misma metodología del proyecto “Evaluación del efecto de la concentración de óxido de cobre (x) en mezclas con dióxido de titanio 〖(TiO_2)〗_((1-x)) (〖CuO)〗_((x)) sobre la actividad microbicida en presencia de luz visible”. Se realizaron tres mezclas por impregnación húmeda, cada una con un porcentaje de sulfato de cobre (precursor del óxido de cobre) diferente, fueron 0.62%, 1.56% y 2.49%. Se realiza una prueba preliminar para probar su funcionalidad, se degrada azul de metileno. Se obtiene que la mezcla con 0.62% de precursor es la que mejor degrada azul de metileno. La inactivación de E. coli se realiza con la película de 2.49% en dos medios de cultivo (agar nutritivo, agar tripticasa soya), obteniendo porcentajes de inactivación del 32,5% al 38%. El método seguido no resulta repetible ni reproducible, los resultados comparados a los obtenidos por Miguel Chávez y Gabriel Vivas usando la misma metodología no concuerdan. Sin embargo el uso de diferentes medios de cultivo no altera el resultado.
Abstract: In this project it was validated that titanium dioxide films in a mixture with copper oxide inactivated 99.99% of E. coli bacteria continuing the same methodology of the project "Evaluation of the effect of copper oxide concentration (x) in mixtures with titanium dioxide (TiO2)(1-x) (CuO)(x) on the microbicidal activity in presence of visible light ". The samples were 0.62%, 1.56% and 2.49% separately, were 0.62%, 1.56% and 2.49%. A preliminary test is carried out to prove its functionality, methylene blue is degraded. It is obtained that the mixture with 0.62% of precursor is the one that best degrades methylene blue. Inactivation of E. coli was performed with the 2.49% film on two culture media (nutritive agar, trypticase soy agar), obtaining percentages of inactivation from 32.5% to 38%. The method followed is not repeatable or reproducible, the results were compared with those obtained by Miguel Chávez and Gabriel Vivas using the same Methodology do not agree. However, the use of different culture media does not alter the result.
URI: http://hdl.handle.net/20.500.11839/6696
Citation: APA 6th - Bohórquez Moreno, P. M. y Gamboa Borrego, M. C. (2018) Validación del efecto de la concentración de óxido de cobre (x) en mezcla con dióxido de titanio (tio2)(1-x) (cuo)(x) para la inactivación fotocatalítica de e. coli en presencia de luz visible (Trabajo de grado). Fundación Universidad de América. Retrieved from http://hdl.handle.net/20.500.11839/6696
Appears in Collections:Trabajos de grado - Ingeniería Química

Files in This Item:
File Description SizeFormat 
6122847-2018-1-IQ.pdf2.6 MBAdobe PDFView/Open


This item is licensed under a Creative Commons Licence Creative Commons