Title: Desarrollo de un tensioactivo catiónico para fibras acrílicas mediante el proceso de sol-gel a nivel laboratorio
Authors: Alarcón Garzón, Daniel Felipe
Estrada Andrade, Andrea Carolina
Thesis advisor: Espinosa, David
License type: Atribución – No comercial – Compartir igual
Keywords: Tensioactivo catiónico;Fibra acrílica;Impregnación suavizante;Cationic surfactant;Acrylic fiber;Softening impregnation;Tesis y disertaciones académicas
Issue Date: 18-Aug-2017
Publisher: Fundación Universidad de América
Resumen: Para el desarrollo de esta investigación se seleccionaron tres materias primas diferentes como son el antiestático, el humectante y TiO2 este último compuesto se sintetizó mediante el proceso de sol-gel con el fin de obtener nanopartículas y generar un producto que pueda impartirle a la fibra la propiedad de hidrofilidad. Mediante un diseño de vértices extremos, se realizaron 13 combinaciones con una réplica para la formulación del suavizante, en el cual se variaron las cantidades de las materias primas para cada combinación; en total se prepararon 26 muestras. A cada muestra se le midió el porcentaje de absorción, el tiempo de dispersión de la gota de agua y la suavidad, ya que estas son las variables de respuesta escogidas para determinar el producto final. Luego de tabular y analizar estadísticamente los resultados de las variables estudiadas en cada una de las. muestras, posteriormente se seleccionó una fórmula que cumplió con los límites de aprobación descritos en el presente proyecto.
Abstract: For the development of this research were selected three different raw materials such as the antistatic, the humectant and TiO2 this last compound was synthesized by the process of sol-gel in order to obtain nanoparticles and generate a product that can impart to the fiber Property of hydrophilicity. By an extreme vertex design, 13 combinations were made with a replica for the softener formulation, in which the quantities of the raw materials for each combination were varied; In total 26 samples were prepared. Each sample was measured the percentage of absorption, the time of dispersion of the drop of water and the softness, since these are the response variables chosen to determine the final product. After tabulating and analyzing statistically the results of the variables studied in each of the. Samples, a formula was subsequently selected that complied with the approval limits described in this project.
URI: http://hdl.handle.net/20.500.11839/6588
Citation: APA 6th - Alarcón Garzón, D. F. y Estrada Andrade, A. C. (2017) Desarrollo de un tensioactivo catiónico para fibras acrílicas mediante el proceso de sol-gel a nivel laboratorio (Trabajo de grado). Fundación Universidad de América. Retrieved from http://hdl.handle.net/20.500.11839/6588
Appears in Collections:Trabajos de grado - Ingeniería Química

Files in This Item:
File Description SizeFormat 
6112721-2017-2-IQ.pdf2.59 MBAdobe PDFView/Open


This item is licensed under a Creative Commons Licence Creative Commons