Title: Caracterización de un material compuesto matriz termoestable reforzado con fibra de guadua
Authors: Ramírez Colorado, Jhon William
Triana Arroyave, Ricardo
Thesis advisor: Forero Rubiano, Ricardo Alberto
License type: Atribución – No comercial – Compartir igual
Keywords: Matriz de resina de poliéster;Fibras de guadua;Auadua angustifolia;Polyester resin matrix;Guadua fibers;Guadua angustifolia;Tesis y disertaciones académicas
Issue Date: 18-Aug-2017
Publisher: Fundación Universidad de América
Resumen: En el presente documento se mostrarán las diferentes pruebas realizadas a un material compuesto con matriz de resina de poliéster y reforzado con fibras de guadua. Se le realizaron diferentes procesamientos para la eliminación de la lignina, con el fin de verificar la influencia en el comportamiento del material y se obtuvieron allí diferentes resultados en sus propiedades cualitativas y cuantitativas donde se utilizaron métodos y ensayos como el de Van Soest, pruebas de tensión y análisis SEM. El material compuesto se fabricó por medio de un proceso a molde abierto y utilizando diferentes porcentajes de fibra al 10%, 15% y 20 % de guadua en el polímero. En la sección de des-lignificación, se realizaron pruebas a la guadua tratada con distintos métodos para disminuir su porcentaje de lignina, se identificó que el método menos nocivo es la mezcla del ácido acético y clorito de sodio con el cual se puede mejorar o mantener las propiedades de la guadua para su post procesamiento e inclusión en el compuesto. Se trabajó la guadua en tiras longitudinales cepilladas para facilitar su manipulación. Después de realizados los procesos de des-lignificación se siguió con una molienda de estas tiras y un tamizaje seleccionando un tamaño adecuado con el que se creó el material compuesto; Adicionalmente, se realizó un estudio de análisis de la fibra, por medio de un microscopio de barrido (SEM) donde se encontró que el proceso de clorito de sodio y ácido acético es el que produce una mejor adhesión matriz fibra.
Abstract: The present document will show the different tests carried out at a Composite material with polyester resin matrix and reinforced with Guadua Different procedures were carried out for the elimination of Lignin, in order to verify the influence on the behavior of the material and They obtained different results in their qualitative and quantitative properties Where methods and tests such as Van Soest are used, stress tests And SEM analysis. The composite material by means of a mold process Open and using different percentages of fiber at 10%, 15% and 20% guadua In the polymer In the uninstallation section, tests were performed on the guadua treated with Different methods to decrease their percentage of lignin, it was identified that the Less harmful method is the mixture of acetic acid and sodium chloride with which You can improve or maintain the properties of guadua for your post Processing and inclusion in the compound. We work in guadua in strips Longitudinal brushes for easy manipulation. After the facts De-lignification processes were followed with a milling of these strips and a Screening by selecting an appropriate size with which the material was created Compound; In addition, a fiber analysis study was carried out by means of From a scanning microscope (SEM) where it was found that the chlorite process Sodium and acetic acid is the one that produces better fiber bonding.
URI: http://hdl.handle.net/20.500.11839/6505
Citation: APA 6th - Ramírez Colorado, J. W. y Triana Arroyave, R. (2017) Caracterización de un material compuesto matriz termoestable reforzado con fibra de guadua (Trabajo de grado). Fundación Universidad de América. Retrieved from http://hdl.handle.net/20.500.11839/6505
Appears in Collections:Trabajos de grado - Ingeniería Mecánica

Files in This Item:
File Description SizeFormat 
4111378-2017-2-IM.pdf43.23 MBAdobe PDFView/Open


This item is licensed under a Creative Commons Licence Creative Commons